Beam Polarisation

0.843 Å - Erbium filter

Beam Polarisation with Heusler at 0.843Å/114meV

Erbium filter - code: Er (ID #1) - 0.5mm thick - efficiency: 96% - transmission: 80%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla +0.962 ± 0.005 -0.962 ± 0.005 -?- -?-
8 Tesla -?- -?- +0.976 ± 0.005 -0.976 ± 0.005
6 Tesla +0.949 ± 0.005 -0.949 ± 0.005 +0.973 ± 0.005 -0.973 ± 0.005
2 Tesla +0.949 ± 0.005 -0.949 ± 0.005 +0.973 ± 0.005 -0.973 ± 0.005
1 Tesla +0.947 ± 0.005 -0.947 ± 0.005 +0.968 ± 0.005 -0.968 ± 0.005
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.946 ± 0.005 -0.946 ± 0.005 +0.966 ± 0.005 -0.966 ± 0.005
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.906 ± 0.003 -0.906 ± 0.003 +0.962 ± 0.003 -0.962 ± 0.003

0.759 Å - Erbium filter

Beam Polarisation with Heusler at 0.759Å/140meV

Erbium filter - code: Er (ID #1) - 0.5mm thick - efficiency: 99% - transmission: 83%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla +0.961 ± 0.005 -0.961 ± 0.005 -?- -?-
8 Tesla -?- -?- +0.974 ± 0.005 -0.974 ± 0.005
6 Tesla +0.945 ± 0.005 -0.945 ± 0.005 +0.976 ± 0.005 -0.976 ± 0.005
2 Tesla +0.944 ± 0.005 -0.944 ± 0.005 +0.974 ± 0.005 -0.974 ± 0.005
1 Tesla +0.940 ± 0.005 -0.940 ± 0.005 +0.968 ± 0.005 -0.968 ± 0.005
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.941 ± 0.005 -0.941 ± 0.005 +0.965 ± 0.005 -0.965 ± 0.005
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.891 ± 0.005 -0.891 ± 0.005 +0.956 ± 0.003 -0.956 ± 0.003

0.711 Å - Iridium filter

Beam Polarisation with Heusler at 0.711Å/160meV

Iridium filter - code: Ir (ID #2) - 0.125mm thick - efficiency: 99% - transmission: 86%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla +0.957 ± 0.005 -0.957 ± 0.005 -?- -?-
8 Tesla -?- -?- +0.974 ± 0.005 -0.974 ± 0.005
6 Tesla +0.939 ± 0.005 -0.939 ± 0.005 +0.972 ± 0.005 -0.972 ± 0.005
2 Tesla +0.937 ± 0.005 -0.937 ± 0.005 +0.973 ± 0.005 -0.973 ± 0.005
1 Tesla +0.935 ± 0.005 -0.935 ± 0.005 +0.973 ± 0.005 -0.973 ± 0.005
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.939 ± 0.005 -0.939 ± 0.005 +0.966 ± 0.005 -0.966 ± 0.005
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.890 ± 0.003 -0.890 ± 0.003 +0.961 ± 0.003 -0.961 ± 0.003

0.545 Å - Hafnium filter

Beam Polarisation with Heusler at 0.545Å/272meV

Halfnium filter - code: Hf (ID #7) - 0.2mm thick - efficiency: 99% - transmission: 96%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla +0.941 ± 0.005 -0.941 ± 0.005 -?- -?-
8 Tesla -?- -?- +0.964 ± 0.005 -0.964 ± 0.005
6 Tesla +0.904 ± 0.005 -0.904 ± 0.005 +0.966 ± 0.005 -0.966 ± 0.005
2 Tesla +0.903 ± 0.005 -0.903 ± 0.005 +0.964 ± 0.005 -0.964 ± 0.005
1 Tesla +0.897 ± 0.005 -0.897 ± 0.005 +0.963 ± 0.005 -0.963 ± 0.005
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.912 ± 0.005 -0.912 ± 0.005 +0.958 ± 0.005 -0.958 ± 0.005
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.845 ± 0.003 -0.845 ± 0.003 +0.951 ± 0.003 -0.951 ± 0.003

0.514 Å - Rhodium filter

Beam Polarisation with Heusler at 0.514Å/306meV

Rhodium filter - code: Rh (ID #3) - 0.125mm thick - efficiency: 98% - transmission: 93%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla -?- -?- -?- -?-
8 Tesla -?- -?- -?- -?-
6 Tesla -?- -?- -?- -?-
2 Tesla -?- -?- -?- -?-
1 Tesla -?- -?- -?- -?-
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
-?- -?- -?- -?-
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
-?- -?- -?- -?-

0.502 Å - Iridium filter

Beam Polarisation with Heusler at 0.502Å/321meV

Iridium filter - code: Ir (ID #2) - 0.125mm thick - efficiency: 99% - transmission: 86%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla +0.929 ± 0.005 -0.929 ± 0.005 -?- -?-
8 Tesla -?- -?- +0.968 ± 0.005 -0.968 ± 0.005
6 Tesla +0.892 ± 0.005 -0.892 ± 0.005 +0.962 ± 0.005 -0.962 ± 0.005
2 Tesla +0.890 ± 0.005 -0.890 ± 0.005 +0.964 ± 0.005 -0.964 ± 0.005
1 Tesla +0.885 ± 0.005 -0.885 ± 0.005 +0.957 ± 0.005 -0.957 ± 0.005
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.906 ± 0.005 -0.906 ± 0.005 +0.957 ± 0.005 -0.957 ± 0.005
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.830 ± 0.003 -0.830 ± 0.003 +0.953 ± 0.003 -0.953 ± 0.003

0.477 Å - Indium filter

Beam Polarisation with Heusler at 0.477Å/355meV

Indium filter - code: In (ID #4) - 0.04mm thick - efficiency: 99% - transmission: 98%

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla -?- -?- -?- -?-
8 Tesla -?- -?- -?- -?-
6 Tesla -?- -?- -?- -?-
2 Tesla -?- -?- -?- -?-
1 Tesla -?- -?- -?- -?-
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
-?- -?- -?- -?-
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
-?- -?- -?- -?-

0.420 Å - Empty (no filter)

Beam Polarisation with Heusler at 0.420Å/458meV

No filter - code: Ey (ID #2)

... with the 10 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
10 Tesla +0.898 ± 0.005 -0.884 ± 0.005 -?- -?-
8 Tesla -?- -?- +0.964 ± 0.005 -0.964 ± 0.005
6 Tesla +0.855 ± 0.005 -0.855 ± 0.005 +0.966 ± 0.005 -0.966 ± 0.005
2 Tesla +0.857 ± 0.005 -0.857 ± 0.005 +0.964 ± 0.005 -0.964 ± 0.005
1 Tesla +0.844 ± 0.005 -0.844 ± 0.005 +0.961 ± 0.005 -0.961 ± 0.005
... with the 2.5 Tesla cryomagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
2.5 Tesla -?- -?- -?- -?-
2.0 Tesla -?- -?- -?- -?-
1.5 Tesla -?- -?- -?- -?-
1.0 Tesla -?- -?- -?- -?-
0.5 Tesla -?- -?- -?- -?-
... with the electromagnet
Applied Field (+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
0.6 Tesla -?- -?- -?- -?-
0.3 Tesla -?- -?- -?- -?-
0.1 Tesla -?- -?- -?- -?-
0.05 Tesla -?- -?- -?- -?-
0.01 Tesla -?- -?- -?- -?-
... with Cryopad
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.884 ± 0.005 -0.884 ± 0.005 +0.963 ± 0.005 -0.963 ± 0.005
... with PNPI fission chamber (18x30 mm² beam)
(+) Polar. / H4A (-) Polar. / H4A (+) Polar. / H4B (-) Polar. / H4B
+0.791 ± 0.003 -0.791 ± 0.003 +0.939 ± 0.003 -0.939 ± 0.003