The prototype cell was tested successfully on D11 in June and July 2015 and several versions are being manufactured: 50 MPa for Spin-Echo providing Ø30 mm incident beam access (see cell 22PL05AO4 ) 300 ... for SANS providing Ø10 mm incident beam access (2 copies, see cell 21PL30AO2 ) 500 MPa for SANS (2 copies) JRA series: A new Pressure Cell for ...

This cell is made from TiZr alloy and provides a Ø12 x 56 mm3 sample volume, i.e. 6.3 ml. A separator may be used when the amount of available sample is low (6 ml required). It can also be provided with ... without separator. The maximum pressure is 600 MPa, i.e. 6 kbar up to 100°C. Dimensions of the TiZr cell in the beam Aluminium inserts making ...

maximum pressure is 250 MPa, i.e. 2.5 kbar up to 100°C. Sketch of the TiZr cell in the beam (pdf - 1.18 Mi) Drawing of the TiZr cell - Click on the image to download the corresponding PDF file ... This cell is made from TiZr alloy and provides a Ø12 x 56 mm3 sample volume, i.e. 6.3 ml. A separator may be used when the amount of available sample is ...

This cell is made from hardened CuBe and provides a Ø12 x 56 mm3 sample volume, i.e. 6.3 ml. A separator may be used when the amount of available sample is low (6 ml required). It can also be provided

This cell is made from the aluminium alloy 7049A-T6 and provides a Ø12 x 56 mm3 sample volume, i.e. 6.3 ml. A separator may be used when the amount of available sample is low (6 ml required). It can also

This cell is made from the aluminium alloy 7049A-T6 and provides a Ø6 x 60 mm3 sample volume, i.e. 1.7 ml. A separator may be used when the amount of available sample is low (1.2 ml required). The pressure

This cell is made from TiZr alloy and provides a Ø6 x 60 mm3 sample volume, i.e. 1.7 ml. A separator may be used when the amount of available sample is low (1.2 ml required). The pressure is generated

This cell is made from the aluminium alloy 7049A-T6 and provides a Ø6 x 60 mm3 sample volume, i.e. 1.7 ml. A separator may be used when the amount of available sample is low (1.2 ml required). The pressure

This cell is made from hardened CuBe and provides a Ø6 x 60 mm3 sample volume, i.e. 1.7 ml. A separator may be used when the amount of available sample is low (1.2 ml required). The pressure is generated