This cell is made from the aluminium alloy 7049A-T6 and provides a Ø6 x 60 mm3 sample volume, i.e. 1.7 ml. A separator may be used when the amount of available sample is low (1.2 ml required). The pressure

This cell is made from hardened CuBe and provides a Ø6 x 60 mm3 sample volume, i.e. 1.7 ml. A separator may be used when the amount of available sample is low (1.2 ml required). The pressure is generated

The prototype cell was tested successfully on D11 in June and July 2015 and several versions are being manufactured: 50 MPa for Spin-Echo providing Ø30 mm incident beam access (see cell 22PL05AO4 ) 300 ... This 300 MPa (3 kbar) cell was designed within the framwork of NMI3-II . The prototype is essentially made from hardened CuBe alloy and Sapphire ...

mK stability). The cell was tested successfully on IN15 in March 2017 (photo below). The transmission is 6Å cell 87% at 6 Å, 79% at 10 Å and 69% at 16 Å. Several variations of this cell have been produced ... providing Ø30 mm incident beam access (this cell) 300 MPa for SANS providing Ø10 mm incident beam access (2 copies, see cell 21PL30AO2 ) 500 ...

This cell is made from the aluminium alloy 7049A-T6 and provides a Ø6 x 60 mm 3 sample volume, i.e. 1.85 ml. The pressure is generated using a hydraulic press with or without external separator. The maximum

This cell is made from TiZr alloy and provides a Ø6 x 62 mm3 sample volume, i.e. 1.75 ml. A separator may be used when the amount of available sample is low (1.3 ml required). The pressure is generated

This cell is made from hardened CuBe and provides a Ø6 x 65 mm3 sample volume i.e. 1.8 ml. A separator may be used when the amount of available sample is low (1.3 ml required). The pressure is generated

This cell is made from TiZr alloy and provides a Ø12 x 44 mm3 sample volume, i.e. 5 ml. The pressure is generated using a hydraulic press with or without separator. The maximum pressure is 700 MPa, i.e

This cell is made from the aluminium alloy 7049A-T6 and provides a Ø12 x 42 mm3 sample volume, i.e. 4.7 ml. The pressure is generated using a hydraulic press with or without separator. The maximum pressure

For liquid pressure cell, with heated two-way capillaries Type Stick for Orange Ø49 Tmin 1.5K Tmax 320K Instrument Pool Sensor Samp. CO/PTO Serial number - Calibration - Interpol. Table -